Method of manufacturing a semiconductor device

ABSTRACT

A method of manufacturing a semiconductor device according to this invention is characterized by including the steps of a) forming, on one major surface of a substrate, a gate structure constituted by either one of a dummy gate electrode and a gate electrode having an insulating film at least on bottom surface, and a device isolation insulating film so as to form a first groove divided by the dummy gate electrode or the gate electrode, to position the dummy gate electrode or the gate electrode in the first groove, and to form the gate structure to have an upper surface level not higher than an upper level of the device isolation insulating film, and b) forming source and drain electrodes in the first groove.

BACKGROUND OF THE INVENTION

The present invention relates to a semiconductor device and a method ofmanufacturing the same.

Recently, demands have arisen for higher integration degree of LSIs andhigher operation speeds thereof. To achieve this purpose, the sizes ofrespective members constituting a transistor are proportionally reduced.However, a reduction in gate electrode width to about 0.1 μm poses thefollowing problems.

FIG. 1 is a sectional view schematically showing an example of aconventional MOSFET. In FIG. 1, e.g., an SiO₂ gate insulating film 2,and a gate electrode 3 prepared by heavily doping an n-type impuritysuch as phosphorus in polysilicon at 2×10²⁰ cm⁻³ or more aresequentially stacked on one major surface of a p-type silicon substrate1. An insulating gate sidewall 4 is formed on the side surface of thegate electrode 3 via a thermal oxidized film 10. An n-type impuritydiffusion region 5 called an extension formed to be shallow below thegate sidewall 4, an n-type impurity diffusion region 6 formed to bedeeper than the extension 5, and a device isolation region 7 made of,e.g., SiO₂ are formed in the surface region of the substrate 1. And ametal silicide layer 8 is formed on the source/drain region by SALICIDE(Self Align Silicide) method to reduce the resistance value of thesource/drain diffusion layers. In the MOSFET shown in FIG. 1, theextension 5 and the n-type impurity diffusion region 6 serve as sourceand drain diffusion layer. The metal silicide layer 8 is also formed onthe gate electrode 3.

In the MOSFET shown in FIG. 1, the extension 5 must be controlled tohave a high impurity concentration of about 10¹⁹ cm⁻³ and a small depthof 0.05 μm or less in order to suppress increases in short channeleffect and electrical resistance value. To make the extension 5 shallow,the ion implantation acceleration voltage must be controlled to be aslow as several keV. However, at a low acceleration voltage, the ioncurrent decreases, so ion implantation cannot be complete within anactual processing time.

To prevent the leakage current from increasing by a reverse bias at ap-n junction, the distance must be typically set to 0.07 μm or morebetween the bottom surface of the metal silicide layer 8 formed in thesurface region of the substrate 1, and the bottom surface of the n-typeimpurity diffusion region 6. The thickness of the metal silicide layer 8is determined such that the parasitic resistance value of thesource/drain diffusion layer becomes much smaller than the resistancevalue upon continuous application of a voltage to the gate electrode 3.For this reason, the metal silicide layer 8 must be formed to apredetermined thickness for obtaining lower resistance value, e.g., 0.05μm or more. In other words, the n-type impurity diffusion region 6 isformed to position its bottom surface at a depth of 0.12 μm or more fromthe surface of the substrate 1. In this case, however, so-calledpunch-through may occur to flow a current even upon no application ofany voltage to the gate electrode 3, i.e., in an OFF state.

As a structure for preventing the punch-through, an elevatedsource/drain structure shown in FIG. 2B is known.

FIGS. 2A and 2B are sectional views, respectively, schematically showingthe steps in manufacturing a conventional MOSFET having an elevatedsource/drain structure. The same reference numerals as in the MOSFETshown in FIG. 1 denote the same parts in the MOSFET shown in FIGS. 2Aand 2B, and a description thereof will be omitted.

In manufacturing a conventional MOSFET having an elevated source/drainstructure, Si is selectively epitaxially grown on an n-type impuritydiffusion region 5 to form an Si film 9, as shown in FIG. 2A. That is, aregion serving as a source/drain diffusion layer is extended to above asubstrate 1. The Si film 9 is also formed on a gate electrode 3. Asshown in FIG. 2B, ions are implanted to form an n-type impuritydiffusion region 6. Further, as described with reference to FIG. 1, ametal silicide layer (not shown) is formed to obtain a MOSFET. In FIGS.2A and 2B, the gate electrode 3 is formed to be lower than a gatesidewall 4 in order to prevent electrical connection between the gateelectrode 3 and the source/drain region due to the lateral growth of theSi film 9 formed on the gate electrode 3.

In the MOSFET formed in this manner, although the n-type impuritydiffusion region 6 is formed to a satisfactory thickness, its effectivedepth, i.e., the depth from the surface of the substrate 1 is smallerthan that in the MOSFET shown in FIG. 1. More specifically, according tothe MOSFET shown in FIGS. 2A and 2B, a larger distance can be setbetween the bottom surface of the metal silicide layer (not shown) andthe bottom surface of the n-type impurity diffusion region 6. By thismethod, however, Si grows not only on the n-type impurity diffusionregion 5 shown in FIG. 2A but also in the lateral direction. As aresult, the Si film 9 is also formed on a device isolation region 7,making it difficult to maintain an insulating state between adjacenttransistors.

Although the nMOS has been exemplified, the pMOS also has the samestructure as that of the nMOS except for an opposite semiconductorconductivity type. Therefore, the above-described problems also occur inthe pMOS.

BRIEF SUMMARY OF THE INVENTION

It is an object of the present invention to provide a semiconductordevice capable of reducing its size and preventing punch-through, and amethod of manufacturing the same.

It is another object of the present invention to provide a semiconductordevice capable of maintaining an insulating state between devices evenupon a reduction in size, and a method of manufacturing the same.

It is still another object of the present invention to provide asemiconductor device capable of reducing its size, preventingpunch-through, and maintaining an insulating state between devices, anda method of manufacturing the same.

According to the present invention, there is provided a method ofmanufacturing a semiconductor device, comprising the steps of a)forming, on one major surface of a substrate, a gate structureconstituted by either one of a dummy gate electrode and a gate electrodehaving an insulating film at least on bottom surface, and a deviceisolation insulating film so as to form a first groove divided by thedummy gate electrode or the gate electrode, to position the dummy gateelectrode or the gate electrode in the first groove, and to form thegate structure to have an upper surface level not higher than an upperlevel of the device isolation insulating film, and b) forming source anddrain electrodes in the first groove.

According to the present invention, there is also provided a method ofmanufacturing a semiconductor device, comprising the steps of forming adummy gate wiring layer on one major surface of a substrate, forming asemiconductor film on an exposed surface of one major surface of asubstrate, forming a semiconductor film on an exposed surface of onemajor surface of the substrate by using epitaxial growth, and forming,on the semiconductor film, a gate sidewall which is made of an insulatorand covers a side surface of the dummy gate wiring layer.

According to the present invention, there is further provided asemiconductor device comprising a substrate, a device isolationinsulating film formed on one major surface of the substrate, a gateelectrode formed on one major surface of the substrate, a gate wiringlayer formed on the device isolation insulating film and connected tothe gate electrode, a source electrode and drain electrode arranged onone major surface of the substrate to face each other via the gateelectrode, and an insulating film formed on a bottom surface and a sidesurface of the gate electrode and the gate wiring layer, and wherein thegate electrode, the gate wiring layer, the source electrode, and thedrain electrode have upper surface levels equal to or lower than anupper surface level of the device isolation insulating film.

According to the present invention, there is still further provided asemiconductor device comprising a substrate, a gate wiring layer formedon one major surface of the substrate, an insulating film formed betweenthe substrate and the gate wiring layer and on a side surface of thegate wiring layer, a pair of thin films formed by epitaxial growing asemiconductor on one major surface of the substrate, and arranged on twosides of the gate wiring layer, and a gate sidewall formed on the pairof thin films, covering the side surface of the gate wiring layer, andmade of an insulator.

Additional objects and advantages of the invention will be set forth inthe description which follows, and in part will be obvious from thedescription, or may be learned by practice of the invention. The objectsand advantages of the invention may be realized and obtained by means ofthe instrumentalities and combinations particularly pointed outhereinafter.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING

The accompanying drawings, which are incorporated in and constitute apart of the specification, illustrate presently preferred embodiments ofthe invention, and together with the general description given above andthe detailed description of the preferred embodiments given below, serveto explain the principles of the invention.

FIG. 1 is a sectional view schematically showing a conventional MOSFET;

FIGS. 2A and 2B are sectional views, respectively, schematically showingthe steps in manufacturing a conventional MOSFET having an elevatedsource/drain structure;

FIGS. 3A to 3K are perspective views, respectively, schematicallyshowing the manufacturing steps according to the first embodiment of thepresent invention;

FIG. 4A is a perspective view schematically showing the manufacturingstep according to the first embodiment of the present invention;

FIGS. 4B to 4C are sectional views taken along the lines 4B—4B and 4C—4Cin FIG. 4A, respectively;

FIGS. 5A to 5C are sectional views, respectively, schematically showingthe manufacturing steps according to the first embodiment of the presentinvention;

FIG. 6 is a perspective view showing a semiconductor device according tothe first embodiment of the present invention;

FIGS. 7A to 7D are sectional views, respectively, schematically showingthe manufacturing steps according to the second embodiment of thepresent invention;

FIGS. 8A to 8F are perspective views, respectively, schematicallyshowing the manufacturing steps according to the third embodiment of thepresent invention;

FIGS. 9A to 9H are perspective views, respectively, schematicallyshowing the manufacturing steps according to the fourth embodiment ofthe present invention;

FIGS. 10A to 10E are perspective views, respectively, schematicallyshowing the manufacturing steps according to the fifth embodiment of thepresent invention;

FIGS. 11A to 11F are views, respectively, schematically showing themanufacturing steps according to the seventh embodiment of the presentinvention;

FIGS. 12A to 12F are perspective views, respectively, schematicallyshowing the manufacturing steps according to the eighth embodiment ofthe present invention;

FIGS. 13A to 13R are views, respectively, schematically showing thesteps in manufacturing a semiconductor device according to the ninthembodiment of the present invention;

FIGS. 14A to 14R are views, respectively, schematically showing thesteps in manufacturing a semiconductor device according to the 10thembodiment of the present invention;

FIGS. 15A to 15E are plan views, respectively, schematically showing thesteps in manufacturing the semiconductor device according to the 10thembodiment of the present invention;

FIGS. 16A to 16X are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 11th embodiment of the present invention;

FIGS. 17A to 17H are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 12th embodiment of the present invention;

FIGS. 18A and 18B are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 13th embodiment of the present invention;

FIGS. 19A and 19B are sectional views, respectively, schematicallyshowing a method of manufacturing a semiconductor device according tothe ninth to 13th embodiments of the present invention;

FIG. 20A is a sectional view schematically showing a method ofmanufacturing a conventional MOSFET;

FIG. 20B is a sectional view schematically showing a method ofmanufacturing a MOSFET according to the first to 13th embodiments of thepresent invention;

FIGS. 21A and 21B are graphs, respectively, showing the relationshipbetween the width of the device isolation region and the short yield inthe MOSFETs shown in FIGS. 20A and 20B;

FIGS. 22A to 22K are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 14th embodiment of the present invention; and

FIGS. 23A to 23D are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 15th embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

The present invention will be described below with reference to theseveral views of the accompanying drawing.

The first embodiment will be explained.

FIGS. 3A to 3K are perspective views, respectively, schematicallyshowing the manufacturing steps according to the first embodiment of thepresent invention. The first embodiment will be described with referenceto FIGS. 3A to 3K.

As shown in FIG. 3A, a thermal oxide film 12 having a thickness of about5 nm is formed on an exposed (100) face of a silicon substrate 11.Silicon nitride is deposited by LPCVD on the thermal oxide film 12 toform a silicon nitride film 13 having a thickness of about 150 nm.

A resist pattern (not shown) is formed on the silicon nitride film 13 byphotolithography or EB lithography. As shown in FIG. 3B, the siliconnitride film 13, the oxide film 12, and the silicon substrate 11 areetched by RIE (Reactive Ion Etching) to form a device region 15. Agroove 14 formed at this time is used for device isolation (STI: SallowTrench Isolation). The trench depth is set to about 300 nm.

Then, the groove 14 is filled with a TEOS-based oxide by forming aTEOS-based oxide film 16 to a thickness of, e.g., about 600 nm by CVD onthe surface of the substrate 11 in which the groove 14 is formed. Asshown in FIG. 3C, the TEOS-based oxide film 16 is flattened by CMP(Chemical Mechanical Polishing). At this time, since the silicon nitridefilm 13 functions as a stopper film, the polishing of the TEOS-basedoxide film 16 by CMP can be stopped when the silicon nitride film 13 isexposed. The silicon nitride film 13 becomes slightly thin upon CMP butis left by about 130 nm by controlling CMP conditions.

As shown in FIG. 3D, a groove 17 is formed to bury a gate electrode bythe following method. First, a resist pattern (not shown) is formed byphotolithography or EB lithography on a region except for a gateelectrode formation region. The silicon nitride film 13 and the TEOSoxide film 16 formed in the gate electrode formation region are etchedand removed by RIE. If necessary, a poly-silicon film may be formedbelow the silicon nitride film 13. In this case, an RIE of the siliconnitride film can be stopped when the poly-silicon film is exposed.

The groove 17 is preferably formed to the same depth as the thickness ofthe silicon nitride film 13. If RIE is separately performed for thesilicon nitride film 13 and the oxide film 16 under the conditionswherein a satisfactory etching selectivity can be obtained, thefollowing merits can be attained. This will be explained with referenceto FIGS. 4A to 4C.

FIG. 4A schematically shows the same step as that shown in FIG. 3D.FIGS. 4B and 4C are sectional views taken along the lines 4B—4B and4C—4C in FIG. 4A, respectively.

As shown in FIG. 4B, when RIE is performed for the TEOS oxide film 16and then the nitride film 13, the thermal oxide film 12 is left belowthe nitride film 13 to prevent the silicon substrate 11 from beingdamaged by RIE. RIE is relatively slightly performed for the TEOS oxidefilm 16 and stops before the side surface of the device isolation grooveis exposed. With this processing, no parasitic transistor is formed at achannel edge upon forming a transistor.

As shown in FIG. 4C, when RIE is performed for the nitride film 13 andthen the oxide film 16, the oxide film 12 below the nitride film 13 isremoved, so the silicon substrate 11 is damaged by RIE. Also when RIE issimultaneously performed for the nitride film 13 and the oxide film 16under the conditions wherein no satisfactory etching selectivity isobtained between the nitride film and the oxide film, the oxide film 12is removed, and the silicon substrate 11 is damaged by RIE. In thiscase, a parasitic transistor is formed at a channel edge to degrade thedevice characteristics.

The description of the manufacturing steps shown in FIGS. 3A to 3K willbe referred to again. As shown in FIG. 3E, the groove 17 is filled withpolysilicon by forming a polysilicon film 18 to a thickness of about 300nm by LPCVD on the surface of the substrate 11 in which the groove 17 isformed. Further, the polysilicon film 18 is left in only the groove 17by CMP. This polysilicon film 18 is used as a dummy gate wiring layer.In this way, the upper surface levels of the polysilicon film 18, theTEOS oxide film 16, and the silicon nitride film 13 are aligned witheach other to realize a completely flat surface. In this step, CMPconditions are controlled to leave the silicon nitride film 13 and thepolysilicon film 18 to a thickness of about 110 nm.

As shown in FIG. 3F, the silicon nitride film 13 is removed by etchingwith hot phosphoric acid, thereby forming a groove 19. As a result, thelevel of the polysilicon film 18 serving as a dummy gate electrode isaligned with the level of the TEOS oxide film 16 constituting a deviceisolation region, obtaining a structure in which source and drainelectrode formation regions are recessed.

As shown in FIG. 3G, the side and upper surfaces of the polysilicon film18 are oxidized to form oxide films 20 having a thickness of about 4 nm.

As shown in FIG. 3H, a silicon nitride film 21 having a thickness ofabout 15 to 20 nm is formed by LPCVD on the surface of the siliconsubstrate 11 in which the groove 19 is formed. While being selectivelyleft on the sidewall of the groove (the sidewalls of the polysiliconfilm 18 and the TEOS oxide film 16), the silicon nitride film 21 isremoved from the remaining region by entire surface RIE. After that,source and drain diffusion layers (not shown) are formed in surfaceregions positioned at the bottoms of the grooves in the siliconsubstrate 11. As the formation method, ion implantation, solid phasediffusion, vapor phase diffusion, or the like is available. Ifnecessary, an elevated source/drain structure in which a source/drainformation region made of silicon is elevated may be formed by epitaxialgrowth.

As shown in FIG. 3I, the thermal oxide film 12 is removed from thesource/drain region by RIE or the like to expose the silicon surface. Asilicide is sputtered to form a silicide (Co silicide or Ti silicide)film 22 having a thickness of about 100 nm. The silicide on thepolysilicon film 18 (on the gate region) and on the TEOS oxide film 16(on the device isolation region) is removed by CMP, thereby leaving thesilicide 22 on only the source/drain region. Consequently, the silicidefilm 22 can be self-aligned on the source/drain region withoutsilicidation annealing. Therefore, crystal defects can be reduced.

Instead of burying the silicide film as in the first embodiment, atungsten film may be buried because any metal including not only asilicide but also tungsten may be directly adhered to the source/drainregion in order to reduce the resistance of the source/drain region. Atransistor formed in this manner exhibits good electricalcharacteristics at high speeds because of a small resistance in thesource/drain region. In the following description, the silicide isadhered to the source/drain region, which also applies to tungsten.

After the silicide film 22 is buried in the step of FIG. 3I, thesilicide film 22 on the source/drain region may be recessed by about 50nm by etching (i.e., the silicide film 22 has a thickness of about 50nm), and the formed groove may be filled by LPCVD and CMP with aTEOS-based oxide film 31 serving as a cap film, as needed (FIGS. 5A to5C).

In the first embodiment, after the step shown in FIG. 3I, thepolysilicon film 18 serving as a dummy gate wiring layer is removed byRIE or the like, and the underlaying oxide film 12 is removed by anHF-based etching solution to form a groove 23, as shown in FIG. 3J.

As shown in FIG. 3K, a gate insulating film 24 having an effectivethickness (T_(eff)) of about 3 to 4 nm in conversion into an oxide filmis formed by deposition or thermal oxidization. Since the source/drainregion has already been formed (and activated), and no high-temperaturestep is basically performed after this process step, the gate insulatingfilm 24 can be made of a high-dielectric or ferroelectric film such as aTa₂O₅ film or a (Ba, Sr)TiO₃ film. As a gate electrode (gate wiringlayer), a refractory metal is available. When the gate insulating filmis made of a high-dielectric or ferroelectric film, a gate wiringmaterial must be selected in accordance with the type of gate insulatingfilm in use. As the gate wiring layer, Ru, TiN, Al, and the like can beused. In the first embodiment, the gate insulating film 24 is made of asilicon oxide/nitride film. Subsequently, a barrier metal (TiN ortungsten nitride; not shown) having a thickness of about 5 to 10 nm isformed on the gate insulating film 24. A metal gate wiring material suchas tungsten is deposited on the barrier metal by CVD and flattened byCMP to form a gate wiring layer 25.

If necessary, the metal gate wiring layer 25 is recessed by etching byabout 30 nm (i.e., the metal gate wiring layer 25 has a thickness ofabout 70 nm). In this case, the formed groove is filled with siliconnitride by LPCVD and CMP to form a silicon nitride film serving as a capfilm on the metal gate. By employing this process, even if a contacthole is erroneously formed above the gate wiring layer in the subsequentstep, the silicon nitride film functions as an etching stopper toprevent short-circuiting between another wiring layer and the gatewiring layer.

FIG. 6 shows a case wherein the TEOS oxide film 31 is formed as a capfilm on the source/drain electrode, and a silicon nitride film 32 isformed as a cap film on the gate wiring layer 25.

The subsequent steps follow the general LSI manufacturing process. Morespecifically, e.g., a TEOS interlayer insulating film is deposited, andcontact holes for connecting the gate electrode, the source/drainelectrode, and the upper wiring layer are formed in the interlayerinsulating film. A metal wiring layer made of, e.g., aluminum is formedon the interlayer insulating film in which the contact holes are formed.

The second embodiment of the present invention will be described.

FIGS. 7A to 7D are sectional views, respectively, schematically showingthe manufacturing steps according to the second embodiment of thepresent invention. Note that the steps in the second embodiment are thesame as those in the first embodiment except for only the step shown inFIG. 3I. Only a step corresponding to the step shown in FIG. 3I istherefore explained.

In the second embodiment, as shown in FIG. 7A, a silicide film 22 doesnot completely fill a groove in the source/drain region. For thisreason, the groove formed by the silicide film 22 is filled with a TEOSoxide film 41 by CVD, and its surface is flattened by CMP, as shown inFIG. 7B. If necessary, the silicide film 22 is recessed by about 50 nmafter the step in FIG. 7B, as shown in FIG. 7C. The formed groove isfilled with a TEOS oxide film 42 by CVD and flattened, as shown in FIG.7D. Accordingly, cap films made of the TEOS oxide films 41 and 42 can beformed on the silicide film 22. The subsequent steps are the same asthose in the first embodiment.

In the second embodiment, even when the groove in the source/drainregion cannot be completely filled with the silicide film 22, theremaining groove is filled with the TEOS oxide film to effectivelyprevent adverse influence on the subsequent steps.

The third embodiment of the present invention will be described.

FIGS. 8A to 8F are perspective views, respectively, schematicallyshowing the manufacturing steps according to the third embodiment of thepresent invention. Note that the steps in the third embodiment are thesame as the steps shown in FIGS. 3A to 3D in the first embodiment, andsubsequent steps are different from the steps in the first embodiment.Therefore, steps subsequent to the step shown in FIG. 3D will beexplained.

As shown in FIG. 8A, an oxide film 12 is removed with an HF-basedsolution from the bottom of a groove 17 for burying a gate wiring layer.As shown in FIG. 8B, a gate insulating film 51 is formed. Thereafter, apolysilicon film 52 serving as a gate electrode (gate wiring layer) isformed to a thickness of about 300 nm by LPCVD to fill the groove 17,and is flattened by CMP. The surface levels of the polysilicon film 52,a TEOS oxide film 16, and a silicon nitride film 13 are aligned witheach other to realize a completely flat surface. In CMP, its conditionsare controlled to leave the silicon nitride film 13 and the polysiliconfilm 52 having a thickness of about 100 nm.

As shown in FIG. 8C, the silicon nitride film 13 is removed by etchingwith hot phosphoric acid, thereby forming a groove 19. As a result, thelevel of the polysilicon film 52 serving as a gate wiring layer isaligned with the level of the TEOS oxide film 16 for a device isolationregion. A structure in which only a source/drain electrode formationregion is recessed is formed.

As shown in FIG. 8D, the surface of the polysilicon film 52 is oxidizedto form an oxide film 53 having a thickness of about 4 nm.

As shown in FIG. 8E, a silicon nitride film 21 having a thickness ofabout 15 to 20 nm is formed by LPCVD. While being selectively left onthe sidewall of the groove (the sidewalls of the polysilicon film 52 andthe TEOS oxide film 16), the silicon nitride film 21 is removed from theremaining region by entire surface RIE. After that, source and draindiffusion layers (not shown) are formed. As the formation method, ionimplantation, solid phase diffusion, vapor phase diffusion, and the likeare conceivable. If necessary, an elevated source/drain structure may beformed by epitaxial growth.

As shown in FIG. 8F, the thermal oxide film 12 is removed from thesource/drain region by RIE or the like to expose the silicon surface. Asilicide (Co silicide or Ti silicide) is sputtered to form a silicidefilm 22 having a thickness of about 100 nm. The silicide is removed byCMP from the polysilicon film 52 and the TEOS oxide film 16 (deviceisolation region), thereby leaving the silicide 22 on only thesource/drain region. Consequently, the silicide film 22 can beself-aligned on the source/drain region without silicidation annealing.Therefore, crystal defects can be reduced.

Instead of burying the silicide film in the steps shown in FIGS. 8A to8F, a tungsten film may be buried because a metal such as tungsten maybe directly adhered to the source/drain region in order to reduce theresistance of the source/drain region. A transistor formed in thismanner exhibits high speed and good electrical characteristics becauseof a small resistance in the source/drain region.

The subsequent steps follow the general LSI manufacturing process. Morespecifically, e.g., a TEOS interlayer insulating film is deposited, andcontact holes for connecting the gate wiring layer, the source/drainelectrode, and the upper wiring layer are formed in the interlayerinsulating film. A metal wiring layer made of, e.g., aluminum is formedon the interlayer insulating film in which the contact holes are formed.

As described above, according to the first to third embodiments of thepresent invention, a MOSFET with a source/drain electrode made of asilicide can be obtained without silicidation annealing.

In a micropatterned device, a low-resistance silicide as a compound of arefractory metal and silicon is conventionally used for an electrode(source/drain electrode) on the source/drain region or a gate electrode.In the conventional device, however, dislocations easily occur near theinterface between the silicide and silicon owing to stress along withvolume expansion upon silicidation annealing. These dislocations degradethe reliability of a gate insulating film, and the characteristics of anelectrically active region for forming a p-n junction, such as a channelregion or a source/drain region.

When a source/drain electrode is self-aligned using a low-resistancematerial such as a silicide, the device reliability and thecharacteristics conventionally degrade.

To the contrary, according to the first to third embodiments, a MOSFETwith a source/drain electrode made of a silicide can be obtained withoutsilicidation annealing. By the first to third embodiments, asemiconductor device in which a source/drain electrode can beself-aligned using a low-resistance material such as a silicide, whilethe device reliability and the characteristics can be kept unchanged,and a method of manufacturing the same can be provided.

The fourth embodiment of the present invention will be described.

FIGS. 9A to 9H are perspective views, respectively, schematicallyshowing the manufacturing steps according to the fourth embodiment ofthe present invention. Note that the steps in the fourth embodiment arethe same as the steps shown in FIGS. 3A to 3D in the first embodiment,and subsequent steps are different from the steps in the firstembodiment. Therefore, steps subsequent to the step shown in FIG. 3Dwill be explained.

As shown in FIG. 9A, a hydrogen-containing silicon oxide film (to bereferred to as an FOX film hereinafter) 18 is formed to a thickness ofabout 300 nm to fill a groove 17, and is flattened by CMP. The FOX film18 has a composition of H_(0.5)SiO_(0.5) and is characterized by an HFetching rate higher than that of a general SiO₂ film formed by thermaloxidization. The FOX film 18 left in the groove 17 is used as a dummygate wiring layer.

In this manner, the surface levels of the FOX film 18, a TEOS oxide film16, and a silicon nitride film 13 are aligned with each other to realizea completely flat surface. In CMP, its conditions are controlled toleave the silicon nitride film 13 and the FOX film 18 to a thickness ofabout 110 nm.

As shown in FIG. 9B, the silicon nitride film 13 is removed by etchingwith hot phosphoric acid, thereby forming a groove 19. As a result, thelevel of the FOX film 18 serving as a dummy gate electrode is alignedwith the level of the TEOS oxide film 16 for a device isolation region.A structure in which only a source/drain electrode formation region isrecessed is formed.

As shown in FIG. 9C, a silicon nitride film 21 having a thickness ofabout 10 to 20 nm is formed by LPCVD. While being selectively left onthe sidewall of the groove (the sidewalls of the FOX film 18 and theTEOS oxide film 16), the silicon nitride film 21 is removed from theremaining region by entire surface RIE. At this time, the exposedportion of the oxide film 12 becomes thin or is removed by RIE.Thereafter, the silicon surface is exposed in the groove 19 by RIE orHF-based wet etching within a short time.

As shown in FIG. 9D, a source/drain formation region made of silicon isextended upward by epitaxial growth (a single-crystalline silicon filmis formed). An overgrown portion such as a lateral growth portion 22A isremoved by CMP to leave a crystalline silicon film 22 in only the groove19.

Then, source and drain diffusion layers (not shown) for an nMOS and aPMOS are formed in the crystalline silicon film 22. As the formationmethod, ion implantation, solid phase diffusion, vapor phase diffusion,and the like are conceivable. Further, thermal process for activating aconductive impurity is performed.

In the fourth embodiment, after the step shown in FIG. 9E, the FOX film18 serving as a dummy gate wiring layer is removed by the HF solution orthe like, and the underlaying oxide film 12 is removed by an HF-basedetching solution to form a groove 23, as shown in FIG. 9F. The FOX film18 can be selectively removed because of an HF etching rate higher thanthat of the TEOS-based oxide film 16, as described above.

The portion constituting part of the sidewall of the groove 23 in thenitride film 21 is removed by etching with hot phosphoric acid or thelike. At this time, the upper portion of the remaining nitride film 21may be etched. However, since the nitride film 21 is thin, its etchingtime suffices to be short. Therefore, even if the upper portion of theremaining nitride film 21 is etched, the removal amount is very small,so that the device characteristics are free from any adverse influence.

As shown in FIG. 9G, a gate insulating film 24 having an effectivethickness (T_(eff)) of about 2 to 3 nm in conversion into an oxide filmis formed by deposition or thermal oxidization. Since the source/drainregion has already been formed (and activated), and no step at a hightemperature of 600° C. or more is basically performed after this processstep, the gate insulating film 24 can be made of a high-dielectric orferroelectric film such as a Ta₂O₅ film or a (Ba, Sr)TiO₃ film. As agate electrode (gate wiring layer), a metal material is available. Whenthe gate insulating film is made of a high-dielectric or ferroelectricfilm, a gate wiring material must be selected in accordance with thetype of gate insulating film in use. As the gate wiring layer, Ru, TiN,Al, W, and the like can be used. A TiN film, a WN film, or the like isdesirably formed as a barrier metal between the gate insulating film andthe gate electrode.

In the fourth embodiment, the gate insulating film 24 is made of asilicon oxide/nitride film. As shown in FIG. 9G, a barrier metal (TiN ortungsten nitride; not shown) having a thickness of about 5 to 10 nm isformed on the gate insulating film 24. A metal gate wiring material suchas tungsten is deposited on the barrier metal by CVD and flattened byCMP to form a gate wiring layer 25.

If necessary, the metal gate wiring layer 25 is recessed by etching byabout 30 nm (i.e., the metal gate wiring layer 25 has a thickness ofabout 70 nm). The formed groove is filled with silicon nitride by LPCVDand CMP to form a silicon nitride film serving as a cap film on themetal gate. By employing this process, even if a contact hole iserroneously formed above the gate wiring layer in the subsequent step,the silicon nitride film functions as an etching stopper to preventshort-circuiting between another wiring layer and the gate wiring layer.

FIG. 9H shows a case wherein a silicon nitride film 32 is formed as acap film on the metal gate wiring layer 25.

The subsequent steps follow the general LSI manufacturing process. Morespecifically, e.g., a TEOS interlayer insulating film is deposited, andcontact holes for connecting the gate electrode, the source/drainelectrode, and the upper wiring layer are formed therein. A metal wiringlayer made of, e.g., aluminum is formed on the interlayer insulatingfilm in which the contact holes are formed.

The fifth embodiment of the present invention will be described.

FIGS. 10A to 10E are perspective views, respectively, schematicallyshowing the manufacturing steps according to the fifth embodiment of thepresent invention. Note that the steps in the fifth embodiment are thesame as the steps shown in FIGS. 3A to 3D in the first embodiment, andsubsequent steps are different from the steps in the first embodiment.Therefore, steps subsequent to the step shown in FIG. 3D will beexplained.

As shown in FIG. 10A, an oxide film 12 is removed with an HF-basedsolution from the bottom of a groove 17 for burying a gate electrode. Asshown in FIG. 10B, e.g., an HTO film 24 is formed as a gate insulatingfilm. Thereafter, a polysilicon film 25 serving as a gate electrode(gate wiring layer) is formed to a thickness of about 400 nm by LPCVD tofill the groove 17, and is flattened by CMP. The surface levels of thepolysilicon film 25, a TEOS oxide film 16, and a silicon nitride film 13are aligned with each other to realize a completely flat surface. InCMP, CMP conditions and film formation conditions (film thickness) arecontrolled to leave the silicon nitride film 13 and the polysilicon film25 to a thickness of about 200 nm. If necessary, the polysilicon film 25is doped for an nMOS and a pMOS.

The polysilicon film 25 is recessed by about 50 nm by RIE or CDE (i.e.,the polysilicon film 25 has a thickness of about 150 nm). The formedgroove is filled by LPCVD and CMP with a TEOS-based oxide film 32serving as a cap film.

As shown in FIG. 10C, the silicon nitride film 13 is removed by etchingwith hot phosphoric acid, thereby forming a groove 19. As a result, thelevel of the TEOS-based oxide film 32 serving as a cap film is alignedwith the level of the TEOS oxide film 16 for a device isolation region.A structure in which only a source/drain electrode formation region isrecessed is formed.

As shown in FIG. 10D, SiO₂-RIE is performed for a short time to removethe exposed oxide film 12 and expose the silicon surface in the groove19.

As shown in FIG. 10E, a source/drain formation region made of silicon isextended upward by epitaxial growth (a single-crystalline silicon filmis formed). An overgrown portion such as a lateral growth portion isremoved by CMP to leave a crystalline silicon film 22 in only the groove19.

Then, source and drain regions (not shown) for an nMOS and a PMOS areformed in the crystalline silicon film. As the formation method, ionimplantation, solid phase diffusion, vapor phase diffusion, and the likeare conceivable. Further, thermal process for activating a conductiveimpurity is performed.

The subsequent steps follow the general LSI manufacturing process. Morespecifically, e.g., a TEOS interlayer insulating film is formed, andcontact holes for connecting the gate electrode, the source/drainelectrode, and the upper wiring layer are formed therein. A metal wiringlayer made of, e.g., aluminum is formed on the interlayer insulatingfilm in which the contact holes are formed.

The sixth embodiment of the present invention will be described withreference to FIGS. 9A to 9H.

The steps in the sixth embodiment are the same as those shown in FIGS.3A to 3D except that a polysilicon film 13 is formed in place of thesilicon nitride film 13.

As shown in FIG. 9A, a silicon nitride film 18 is formed to a thicknessof about 300 nm to fill a groove 17, and is flattened by CMP. Thesilicon nitride film 18 is used as a dummy gate wiring layer. In thisway, the surface levels of the silicon nitride film 18, a TEOS oxidefilm 16, and the polysilicon film 13 are aligned with each other torealize a completely flat surface. In CMP, its conditions are controlledto leave the polysilicon film 13 and the silicon nitride film 18 to athickness of about 110 nm.

As shown in FIG. 9B, the polysilicon film 13 is removed by RIE, therebyforming a groove 19. As a result, the level of the silicon nitride film18 serving as a dummy gate wiring layer is aligned with the level of theTEOS oxide film 16 for a device isolation region. A structure in whichonly a source/drain electrode formation region is recessed is formed.

As shown in FIG. 9C, a TEOS-based oxide film 21 having a thickness ofabout 15 to 20 nm is formed by LPCVD. While being selectively left onthe sidewall of the groove (the sidewalls of the silicon nitride film 18and the TEOS-based oxide film 16), the TEOS-based oxide film 21 isremoved from the remaining region by entire surface RIE. At this time,the exposed oxide film 12 becomes thin or is removed by RIE. Thereafter,the silicon surface is exposed in the groove 19 by RIE or HF-based wetetching within a short time.

As shown in FIG. 9D, a source/drain formation region made of silicon isextended upward by epitaxial growth (a single-crystalline silicon filmis formed). An overgrown portion such as a lateral growth portion 22A isremoved by CMP to leave a crystalline silicon film 22 in only the groove19.

Then, source and drain diffusion layers (not shown) for an nMOS and apMOS are formed in the crystalline silicon film 22. As the formationmethod, ion implantation, solid phase diffusion, vapor phase diffusion,and the like are conceivable. Further, thermal process for activating aconductive impurity is performed.

In the sixth embodiment, after the step shown in FIG. 9E, the siliconnitride film 18 serving as a dummy gate wiring layer is removed with hotphosphoric acid to form a groove 23, as shown in FIG. 9F.

The portion constituting part of the sidewall of the groove 23 in theTEOS-based oxide film 21 is removed by etching with HF or the like. Atthis time, the upper portions of the remaining TEOS-based oxide film 21and the TEOS-based oxide film 16 may be etched. However, since theTEOS-based oxide film 21 is thin, its etching time suffices to be short.Therefore, even if the upper portions of the remaining TEOS-based oxidefilm 21 and the TEOS-based oxide film 16 are etched, the removal amountis very small, so that the device characteristics are free from anyadverse influence.

By the same method as described in the fourth embodiment, the structureshown in FIG. 9G or 9H is obtained.

The seventh embodiment of the present invention will be described.

FIGS. 11A to 11F are views, respectively, schematically showing themanufacturing steps according to the seventh embodiment of the presentinvention. Note that the steps in the seventh embodiment are the same asthose in the sixth embodiment up to the step shown in FIG. 9E, andsubsequent steps are different.

The structure shown in FIG. 9E is obtained by the same method asdescribed in the sixth embodiment. FIG. 11A is a sectional view takenalong the line 11A—11A in the semiconductor device shown in FIG. 9E.

As shown in FIG. 11B, a crystalline silicon film 22 is recessed by RIEor the like by about 50 nm. After that, source and drain diffusionlayers (not shown) for an nMOS and a pMOS are formed in the crystallinesilicon film 22. As the formation method, ion implantation, solid phasediffusion, vapor phase diffusion, and the like are conceivable. Further,thermal process for activating a conductive impurity is performed.

As shown in FIG. 11C, the groove formed by the recess is filled with ametal material by forming a metal film 31 made of cobalt silicide,tungsten, or the like by sputtering or CVD. The metal film 31 is left inonly the groove by CMP.

As shown in FIG. 11D, a silicon nitride film 18 serving as a dummy gatewiring layer is removed with hot phosphoric acid to form a groove 23.

The structure shown in FIG. 11E is obtained by the same method describedwith reference to the sixth embodiment. In the seventh embodiment, agate insulating film 24 is made of Ta₂O₅, and a gate wiring layer 25 ismade of Al. If necessary, an SiO₂ film or an SiN film having a thicknessof about 0.5 nm may be formed below the Ta₂O₅ film 24. In this case, thefilm can be formed at low temperature (600° C. or less) by using aradical oxidization or a radical nitrization.

If necessary, as shown in FIG. 11F, the surface of the Al metal gatewiring layer 25 is oxidized to form an alumina (Al₂O₃) film 32 servingas a cap film on the gate wiring layer 25. By employing this process,even if a contact hole is erroneously formed above the gate wiring layerin the subsequent step, the alumina film 32 functions as an etchingstopper to prevent short-circuiting between another wiring layer and thegate wiring layer.

The subsequent steps follow the general LSI manufacturing process. Morespecifically, e.g., a TEOS interlayer insulating film is deposited, andcontact holes for connecting the gate electrode, the source/drainelectrode, and the upper wiring layer are formed therein. A metal wiringlayer made of, e.g., aluminum is formed on the interlayer insulatingfilm.

The eighth embodiment of the present invention will be described withreference to FIGS. 12A to 12F.

FIGS. 12A to 12F are perspective views, respectively, schematicallyshowing the manufacturing steps according to the eighth embodiment ofthe present invention. Note that the steps in the eighth embodiment arethe same as those in the first embodiment up to the step shown in FIG.3D, and subsequent steps are different from the steps in the firstembodiment. The steps subsequent to the step shown in FIG. 3D will beexplained.

After the structure shown in FIG. 3D is formed, a dummy gate wiringlayer 18 is formed in a groove 17, as shown in FIG. 12A. The dummy gatewiring layer 18 can be made of TiN, WN_(x), W, Al, Ge, RuO_(x), or thelike. Since these materials can be easily removed by SH processing, theyare preferably used for the dummy gate wiring layer 18. In the followingdescription, the dummy gate wiring layer 18 is made of germanium.

The germanium film 18 is formed to a thickness of about 300 nm to fillthe groove 17, and is flattened by CMP. Accordingly, the surface levelsof the germanium film 18, a TEOS oxide film 16, and a silicon nitridefilm 13 are aligned with each other to realize a completely flatsurface. In CMP, its conditions are controlled to leave the siliconnitride film 13 and the germanium film 18 to a thickness of about 110nm.

As shown in FIG. 12B, the silicon nitride film 13 is removed by etchingwith hot phosphoric acid, thereby forming a groove 19. The level of thegermanium film 18 is aligned with the level of the TEOS oxide film 16for a device isolation region. A structure in which only a source/drainelectrode formation region is recessed is formed.

As shown in FIG. 12C, a silicon nitride film 21 having a thickness ofabout 10 to 20 nm is formed by LPCVD. The silicon nitride film 21 isselectively left on the sidewall of the groove 19 (the sidewalls of thegermanium film 18 and the TEOS-based oxide film 16) by entire RIE. ByRIE, the exposed oxide film 12 becomes thin or is removed. Thereafter,the silicon surface is exposed in the groove 19 by RIE or HF-based wetetching within a short time.

The obtained structure is cleaned with H₂, and a source/drain formationregion made of silicon is extended upward by epitaxial growth (asingle-crystalline silicon film is formed), as shown in FIG. 12D. Anovergrown portion (not shown) such as a lateral growth portion isremoved by CMP to leave a crystalline silicon film 22 in only the groove19.

Source and drain diffusion layers (not shown) for an nMOS and a pMOS areformed in the crystalline silicon film 22. As the formation method, ionimplantation, solid phase diffusion, vapor phase diffusion, and the likeare conceivable. Further, thermal process (RTA and the like) foractivating a conductive impurity is performed. Ti or Co is sputtered toform a silicide film on the source/drain region.

In the eighth embodiment, after the step shown in FIG. 12D, thegermanium film 18 serving as a dummy gate wiring layer and theunderlaying oxide film 12 are removed by SH processing and HF wetetching to form a groove 23, as shown in FIG. 12E.

The portion constituting part of-the sidewall of the groove 23 in thenitride film 21 is removed by etching with hot phosphoric acid or thelike. At this time, the upper portions of the remaining nitride film 21may be etched. However, since the nitride film 21 is thin, its etchingtime suffices to be short. Therefore, even if the upper portion of theremaining nitride film 21 is etched, the removal amount is very small,so that the device characteristics are free from any adverse influence.

By the same method as described in the fourth embodiment, the structureshown in FIG. 12H is obtained.

If necessary, the surface of the metal gate wiring layer 25 is recessedby about 30 nm by etching (i.e., the metal gate wiring layer 25 has athickness of about 70 nm). The formed groove is filled with siliconnitride by LPCVD and CMP to form a silicon nitride film serving as a capfilm on the metal gate. By adopting this process, even if a contact holeis erroneously formed above the gate wiring layer in the subsequentstep, the silicon nitride film functions as an etching stopper toprevent short-circuiting between another wiring layer and the gatewiring layer.

The subsequent steps follow the general LSI manufacturing process. Morespecifically, e.g., a TEOS interlayer insulating film is deposited, andcontact holes for connecting the gate electrode, the source/drainelectrode, and the upper wiring layer are formed therein. A metal wiringlayer made of, e.g., aluminum is formed on the interlayer insulatingfilm.

According to the first to eighth embodiments described above, prior toformation of the source/drain electrode, the gate structure and thedevice isolation insulating film are so formed as to align their uppersurface levels with each other, and to form a groove crossing the gatestructure and divided by it. The source/drain electrode is formed in thegroove. By the first to eighth embodiments, therefore, the source/drainelectrode can be self-aligned. More specifically, in the first to eighthembodiments, since the upper surface level of the gate structure isequal to the upper surface level of the device isolation insulatingfilm, source/drain electrode can be formed by burying a metal material.In the case where the groove is buried with a silicon by epitaxialgrowth, an overgrown portion such as a lateral growth portion can beremoved by CMP. An insulating state between adjacent transistors can bemaintained, and a high-density micropatterned transistor can berealized.

According to the fourth to eighth embodiments, a concave transistor canbe obtained without RIE for a channel region formation portion of thesubstrate. Therefore, the channel region can be prevented from beingdamaged by RIE in manufacturing a concave transistor. That is,degradation in electrical characteristics of the device can beprevented.

In the first to eighth embodiments, the source/drain electrode can bemade of a silicide by sputtering it without silicidation annealing.Accordingly, degradations in device reliability and characteristics canbe prevented.

In the first to eighth embodiments, when an elevated source/drainstructure is adopted, the source/drain diffusion layers can be madesufficiently thick, and its effective depth of junction can bedecreased. Even upon a reduction in size, punch-through can be preventedand an insulating state between devices can be maintained.

Note that in the first to eighth embodiments, the same referencenumerals denote the same parts unless otherwise specified.

The ninth embodiment of the present invention will be described withreference to FIGS. 13A to 13P.

FIGS. 13A to 13P are views, respectively, schematically showing thesteps in manufacturing a semiconductor device according to the ninthembodiment of the present invention. FIGS. 13A to 13O, 13Q, and 13R aresectional views, and FIG. 13P is a plan view.

As shown in FIG. 13A, a thermal oxide film 102 having a thickness ofabout 4 nm is formed on one surface of a silicon substrate 101. Apolysilicon film 103 having a thickness of about 200 nm is formed on thethermal oxide film 102 by CVD.

As shown in FIG. 13B, the polysilicon film 103, the thermal oxide film102, and the silicon substrate 101 are etched by lithography and RIE toform a groove 104. The groove 104 is used for device isolation later.

As shown in FIG. 13C, a thermal oxide film 105 is formed on the exposedsurfaces of the polysilicon film 103 and the silicon substrate 101.

As shown in FIG. 13D, the groove 104 is filled with silicon oxide byforming a silicon oxide film 106 by CVD on the surface of the substrate101 in which the groove 104 is formed. The silicon oxide film 106 ispolished by CMP. The polishing is stopped when the polysilicon film 103is exposed. Consequently, a device isolation region is formed.

As shown in FIG. 13E, a thermal oxide film 107 is formed on the exposedsurface of the polysilicon film 103, and an SiN film 108 is grown to athickness of about 150 nm on the thermal oxide film 107. The thermaloxide film 107 is used as an etching stopper. While being left in only agate wiring formation region, the SiN film 108 is removed from theremaining region by lithography and RIE.

As shown in FIG. 13F, the exposed portion of the thermal oxide film 107is removed by short-time RIE or wet etching. Using the SiN film 108 andthe silicon oxide film 106 as a mask, the polysilicon film 103 isetched.

In the step shown in FIG. 13B, the groove 104 may be tapered forward. Inthis groove 104, the polysilicon film 103 is left on the sidewall of thesilicon oxide film 106 by the above steps, as shown in FIG. 13G. Sincethis polysilicon film 103 functions as a gate electrode later, it mayincrease the parasitic capacitance between the gate electrode and asource/drain electrode. Accordingly, the taper angle of the groove 104is set such that the entire polysilicon film 103 left on the sidewall ofthe silicon oxide film 106 is changed into an oxide film upon thermaloxidation.

After that, as shown in FIG. 13H, a thermal oxide film 109 having athickness of about 4 nm is formed on the sidewall of the polysiliconfilm 103 in order to protect a gate edge. Note that when the groove 104is tapered forward, the entire polysilicon film 103 left on the sidewallof the silicon oxide film 106 is oxidized. Further, ions are implantedinto the substrate 101 and activated to form an extension in the surfaceregion of the substrate 101. Next, an SiN film is formed by CVD andsubjected to RIE to selectively leave it on only the sidewalls of thepolysilicon film 103, the thermal oxide film 105, the thermal oxide film107, and the SiN film 108, and to form an SiN sidewall 110, as shown inFIG. 13I.

At this time, a deeper diffusion region may be formed in the surfaceregion of the substrate 101 by ion implantation. In the ninthembodiment, since an elevated source/drain structure is to be formed inthe subsequent step, no deep diffusion region need be formed. That is,the extension suffices to be formed. Note that the sidewall 110 isformed to reduce the coupling capacitance between the source/drainelectrode and the gate electrode, and to prevent short-circuitingbetween the source/drain electrode and the gate electrode.

The thermal oxide film 102 exposed by wet processing is removed. Apolysilicon film 111 is formed by CVD, as shown in FIG. 13J, andflattened by CMP or resist etch-back, as shown in FIG. 13K. Thisflattening is performed until the SiN film 108 and the sidewall 110 areexposed. In this way, the entire region except for a gate wiringformation region is covered with the polysilicon film 111. A thermaloxide film (not shown) used as an etching stopper is formed on thesurface of the polysilicon film 111.

As shown in FIG. 13L, part of the sidewall 110 and the SiN film 108 areremoved by wet etching with hot phosphoric acid or the like, radicaletching, or RIE.

The thermal oxide film (not shown) formed on the surface of thepolysilicon film 111, and the thermal oxide film 105 are removed by wetprocessing.

As shown in FIG. 13M, a groove 112 is formed by removing the exposedportion of the silicon oxide film 106 by RIE using the polysilicon films103 and 111 and the SiN sidewall 110 as a mask. The silicon oxide film106 is removed not to expose the channel edge, i.e., the sidewall of thethermal oxide film 102. With this structure, decreases in gate breakdownvoltage and transistor characteristics, which pose problems in aconventional STI structure, can be prevented.

On the surface of the substrate 101 in which the groove 112 is formed, apolysilicon film 113 is grown, as shown in FIG. 13N, and flattened byCMP or resist etch-back, as shown in FIG. 130. This flattening isperformed until the silicon oxide film 106 is exposed.

FIG. 13P is a plan view showing the semiconductor device shown in FIG.130. As shown in FIG. 13P, the gate electrode formation region is formedof the polysilicon film 103, the source/drain electrode formation regionis formed of the polysilicon film 111, and the gate wiring formationregion is formed of the polysilicon film 113. Ions are simultaneouslyimplanted into the polysilicon films 103, 111 and 113 and annealing foractivation is performed. When the diffusion region formed in advancebecomes excessively deep upon this annealing, no extension is formed inadvance. Instead, in this step, an extension is formed bysolid-phase-diffusing an ion-implanted dopant. As a result, an extensioncan be formed to a desired depth.

As shown in FIG. 13Q, silicidation is performed using Co, Ti, or thelike, thereby forming a silicide film 114 in the surface regions of thepolysilicon films 103, 111, and 113. More specifically, a gate electrodeand a source/drain electrode are self-aligned. Note that if the silicidefilm 114 is also formed on the sidewall 110 due to variations inselective reaction, the surface of the resultant structure is slightlypolished by CMP or the like. With this processing, the silicide film 114formed on the sidewall 110 can be easily removed. Alternatively, asshown in FIG. 13R, the polysilicon films 103, 111, and 113 are properlyetched back to make the sidewall 110 project from the polysilicon films103, 111, and 113 before silicidation.

As described above, according to the ninth embodiment, a source/drainregion can be prevented from being formed on STI in forming a MOSFETwhich has an elevated source/drain structure and a source/drainelectrode made of a silicide. In addition, according to this embodiment,since no gate edge is exposed upon etch-back of STI, a MOSFET havinggood electrical characteristics can be obtained.

The 10th embodiment of the present invention will be described. In the10th embodiment, in simultaneously forming a plurality of MOSFETs, thesource or drain electrode of a given MOSFET and the source or drainelectrode of another one, or the source or drain electrode of a certainMOSFET and the gate electrode of another one are electrically connected.

FIGS. 14A to 14R schematically show the steps in manufacturing asemiconductor device according to the 10th embodiment of the presentinvention. The two types of connection described above will be explainedwith reference to FIGS. 14A to 14R.

By the same method as described in the ninth embodiment with referenceto FIGS. 13A to 13I, the structures shown in FIGS. 14A and 14B areobtained. FIG. 14C is a sectional view taken along the line 14C—14C inFIG. 14A, and FIG. 14D is a sectional view taken along the line 14D—14Din FIG. 14B.

By the same steps as described in the ninth embodiment with reference toFIGS. 13J to 13L, the structures shown in FIGS. 14E and 14F areobtained.

Thereafter, as shown in FIGS. 14G and 14H, a resist film 120 is formed,and an opening is formed by lithography. Using the resist film 120 as amask, a polysilicon film 111 is removed to expose a silicon oxide film106. FIGS. 14I and 14J are plan views, respectively, showing thesemiconductor devices shown in FIGS. 14G and 14H.

As shown in FIGS. 14K and 14L, an SiN sidewall 110 is etched by RIE orthe like using a thermal oxide film 105, the polysilicon film 111, andthe resist film 120 as a mask. The SiN sidewall 110 is not necessarilycompletely removed. The SiN sidewall 110 is satisfactorily removed to aposition lower than the bottom surface of a silicide film to be formedin the subsequent step.

Then, the resist film 120 is removed. By the same method as described inthe ninth embodiment with reference to FIG. 13M, the structures shown inFIGS. 14M and 14N are obtained. Further, by the same method as describedin the ninth embodiment with reference to FIGS. 13N to 13Q, thestructures shown in FIGS. 140 and 14P are obtained. FIGS. 14Q and 14Rare plan views, respectively, showing the semiconductor devices shown inFIGS. 140 and 14P.

An application example of the above-described method to manufacture ofan SRAM having a CMOS-6tr-cell structure will be explained below.

FIGS. 15A to 15E are plan views, respectively, schematically showing thesteps in manufacturing a semiconductor device according to the 10thembodiment of the present invention.

The structure shown in FIG. 15A is obtained by the steps described inthe ninth embodiment with reference to FIGS. 13A to 13D. In FIG. 15A, anNMOS device region 152, a pMOS device region 153, and a device isolationregion 154 are formed on a substrate 151.

As shown in FIG. 15B, a gate wiring pattern 155 is formed to connectgate wiring layers of the nMOS and pMOS of inverter circuits 156 in acell, and to form a word line 157.

After that, as shown in FIG. 15C, a junction wiring region pattern 158is formed. Conventionally, in a flip-flop circuit 170, a junction wiring159 for connecting the source/drain electrode of a given device to thatof another device, and a junction wiring 160 for connecting thesource/drain electrode of a certain device to the gate electrode ofanother device are formed in separate layers. More specifically, inorder to form at least one of the junction wiring 159 and 160, one ormore wiring layers must be formed in addition to a layer in which a gatewiring is formed. To the contrary, according to the 10th embodiment, theabove wiring can be formed in the layer in which the gate wiring isformed. Therefore, only a bit line, a V+ line, and a V− line are formedin an upper layer arranged on the gate wiring formation layer. That is,contact regions formed in the gate wiring formation layer are three, abit contact region 161, a V− contact region 162, and a V+ contact region163.

If cells are coupled to each other, as shown in FIG. 15D, the bit line164, the V+ line 165, and the V− line 166 formed in the upper layer arearranged not to cross each other, as shown in FIG. 15E. For this reason,the bit line, the V+ line, and the V− line can be formed in the samelayer. According to the 10th embodiment, therefore, all the wirings ofan SRAM can be formed in the gate wiring layer and one upper wiringlayer.

As described above, according to the 10th embodiment of the presentinvention, a wiring layer for connecting the source/drain electrode of agiven MOSFET to that of another one, and a wiring layer for connectingthe source/drain electrode of a certain MOSFET to the gate electrode ofanother one can be formed in a gate wiring formation layer. Accordingly,the number of steps greatly decreases. In a conventional structure, alarge source/drain region is required to connect the source/drainelectrode of a certain MOSFET to that of another one. In contrast tothis, according to the 10th embodiment, the source/drain region can bereduced in size, compared to the conventional structure. As a result,the transistor characteristics can be improved, while an increase indiffusion capacitance is suppressed.

The 11th embodiment of the present invention will be described below. Inthe ninth embodiment, a source/drain electrode is formed after a gateelectrode is formed in advance. In the 11th embodiment, however, a dummygate wiring layer is formed in place of a gate electrode. According tothe 11th embodiment, a MOSFET having a structure (to be referred to as ahalf-concave structure hereinafter) wherein part of the side surface ofa gate electrode is used as a channel can be manufactured. The 11thembodiment will be described with reference to FIGS. 16A to 16X.

FIGS. 16A to 16X are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 11th embodiment of the present invention.

As shown in FIG. 16A, a thermal oxide film 102 having a thickness ofabout 4 nm is formed on one surface of a silicon substrate 101. Thethermal oxide film 102 is used as an etching stopper in the subsequentstep in order to protect the surface of the substrate 101. A siliconnitride film 103 having a thickness of about 150 nm is formed on thethermal oxide film 102 by CVD.

As shown in FIG. 16B, the silicon nitride film 103, the thermal oxidefilm 102, and the silicon substrate 101 are etched by lithography andRIE to form a groove 104. The groove 104 is used for device isolationlater. In the 11th embodiment, the groove 104 is tapered forward. Athermal oxide film 105 is formed on the exposed surface of the siliconsubstrate 101.

As shown in FIG. 16C, the groove 104 is filled with silicon oxide byforming a silicon oxide film 106 by CVD on the surface of the substrate101 in which the groove 104 is formed. The silicon oxide film 106 ispolished by CMP. This polishing stops when the silicon nitride film 103is exposed. In this way, a device isolation region is formed.

A silicon oxide film 108 having a pattern shown in FIG. 16D is formed toa thickness of about 300 nm on the silicon nitride film 103 and thesilicon oxide film 106. The silicon oxide is used because of its highetching selectivity with respect to the silicon nitride film 103. Notethat in this etching, the silicon oxide film 106 is also partiallyremoved. When the silicon oxide film 106 is removed by an excessivelylarge amount, an SiN film may be formed as an etching stopper betweenthe silicon oxide film 108 and the silicon oxide film 106.

As shown in FIG. 16E, the silicon nitride film 103 is anisotropicallyetched by RIE or the like using the silicon oxide films 106 and 108 as amask and the silicon oxide film 102 as an etching stopper. At this time,the silicon nitride film 103 between the silicon oxide film 106 and thesubstrate 101 in the forward tapered groove 104 is not etched and isleft. That is, an SiN sidewall can be self-aligned around a source/drainelectrode formation region. Therefore, according to the 11th embodiment,no SiN sidewall need be separately formed. When the sidewall is madesufficiently thick, and the STI region is made narrow, the groove 104 isformed as shown in FIG. 16F. In other words, the silicon nitride film103 is etched into a tapered shape, whereas the substrate 101 is etchedinto a rectangular shape.

Then, the exposed portion of the silicon oxide film 102 is removed bywet etching with dilute hydrofluoric acid or the like. As shown in FIG.16G, silicon is epitaxially grown on the exposed surface of thesubstrate 101 to form a crystalline silicon film 130. When a portionaround the exposed surface of the substrate 101 is covered with asilicon oxide film, erroneous growth such as facet growth occurs inepitaxial growth. To the contrary, in the 11th embodiment, since aportion around the exposed surface of the substrate 101 is covered withthe SiN film, the crystalline silicon film 130 can be uniformly formedwith a sufficient thickness without any erroneous growth. Subsequently,a thermal oxide film 131 is formed on the surface of the crystallinesilicon film 130. The thermal oxide film 131 is used as an etchingstopper in the subsequent step.

A conductive impurity is doped in the crystalline silicon film 130 byion implantation or the like, and an activation is performed. Instead ofthe above step, a mixture of a conductive impurity and silicon may beepitaxially grown. If no concave structure is required, no epitaxialgrowth is performed. If an extension is formed at this time, e.g., afterimplanting ions to form the extension, a silicon oxide sidewall isformed, then a diffusion region containing the ions at highconcentration is formed, and the sidewall is removed by wet etching orthe like. The sidewall can be removed by etching within a short time byforming it of, e.g., BPSG whose etching rate is higher than that of ageneral silicon oxide. Therefore, the silicon oxide film 106 can beprevented from being excessively removed. Forming a heavily dopeddiffusion region requires a higher activation temperature than theextension formation temperature. Accordingly, after a sidewall isformed, a heavily doped diffusion region is formed in advance. After thesidewall is removed, ions are implanted and an activation is performedto form an extension as a shallower junction region. With thisprocessing, a shallower junction can be formed.

A polysilicon film 111 is formed by CVD, as shown in FIG. 16H, andflattened by CMP or resist etch-back, as shown in FIG. 16I. Thisflattening is performed until the silicon oxide film 108 is exposed. Asa result, the entire region except for a gate wiring formation region iscovered with the polysilicon film 111. Using the polysilicon film 111 asa mask, a groove can be formed in correspondence with the gate wiringformation region.

As shown in FIG. 16J, the silicon oxide film 108 is removed by RIE orthe like using the polysilicon film 111 as a mask.

As shown in FIG. 16K, the silicon oxide film 106 is etched by RIE or thelike using the silicon nitride film 103 and the polysilicon film 111 asa mask. This etching stops before a channel edge is exposed.

As shown in FIG. 16L, the exposed portion of the silicon nitride film103 is anisotropically etched by RIE or the like using the polysiliconfilm 111 and the thermal oxide film 102 as a mask. At this time, whenthe etching selectivity is low between the silicon nitride film 103 andthe polysilicon film 111, a thermal oxide film is formed on the surfaceof the polysilicon film 111 before RIE, thereby obtaining a sufficientlyhigh etching selectivity.

As shown in FIG. 16M, the thermal oxide film 102 is removed with dilutehydrofluoric acid or the like, and a gate insulating film 132 is formed.The gate insulating film 132 may be formed by thermal oxidization orCVD. Thereafter, a film 113 made of a low-resistance material, e.g., Wis formed. If necessary, a barrier layer is formed on the gateinsulating film 132, and then the W film 113 is formed. Before the gateinsulating film 132 is formed, a thin thermal oxide film may be formedand then removed. Alternatively, hydrogen annealing or the like may beperformed. With this processing, the edge of the crystalline siliconfilm 130 can be rounded. By ion implantation into a channel regionimmediately before formation of the gate insulating film 132, a heavilydoped channel region can be formed at only a desired portion of thedevice region. Therefore, the junction capacitance of the source/drainregion can be reduced.

As shown in FIG. 16N, before forming the gate insulating film 132, aheavily doped channel region 133 may be formed by ion implantation orthe like, and a film 134 made of Si or Si-Ge may be formed by selectiveepitaxial growth. As a result, a MOSFET having a retrograde channelstructure can be obtained. In selective epitaxial growth, although Si orSi-Ge may also be epitaxially grown on the polysilicon film 111, it canbe removed at the same time as etching the polysilicon film 111. FIG.16N is an enlarged view showing the groove.

As shown in FIG. 160, the W film 113 is flattened by CMP, resistetch-back, or the like. This flattening is performed until thepolysilicon film 111 is exposed.

As shown in FIG. 16P, the polysilicon film 111 is etched by RIE or thelike using the silicon oxide film 106, the W film 113, and the gateinsulating film 132 as a mask. This etching need not be anisotropicetching, and may use radical atoms, which prevents the gate edge fromdamage. To repair a damaged gate edge, the obtained structure isoxidized in an atmosphere containing hydrogen, water, and nitrogen.Consequently, the gate edge of the crystalline silicon film 130 can berepaired without oxidizing the W film 113.

As shown in FIG. 16Q, an SiN film is formed and subjected to RIE to forman SiN sidewall 110 for preventing electrical short-circuiting between asource/drain electrode and a gate electrode. Subsequently, the thermaloxide film 131 is removed with dilute hydrofluoric acid or dry etching.Instead of SiN, the sidewall 110 may be made of, e.g., a silicon oxidehaving a lower dielectric constant. With this material, the parasiticcapacitance can be reduced between the source/drain electrode and thegate electrode. In the step shown in FIG. 16G, a conductive impurity isdoped in the crystalline silicon film 130. However, when the gateelectrode is made of a refractory metal such as W, annealing describedwith reference to FIGS. 16M and 16N can be eliminated by performing ionimplantation and activation annealing subsequent to the steps shown inFIGS. 16P and 16Q. Therefore, a shallower junction can be formed.

As shown in FIG. 16R, an Al film 135 is formed and flattened by CMP,resist etch-back, or the like. This flattening is performed until thesilicon oxide film 106 is exposed. As a result, a source/drain electrodeis formed. If necessary, a barrier layer is formed before forming the Alfilm 135.

In the above-described manner, a half-concave MOSFET can be obtained.

According to the 11th embodiment, in simultaneously forming a pluralityof half-concave MOSFETs, the source electrode of a certain MOSFET andthe drain electrode of another one, or the source or drain electrode ofa given MOSFET and the gate electrode of another one can be electricallyconnected. The method will be described below.

After the step shown in FIG. 16Q, as shown in FIG. 16S, a resist film136 is formed, and an opening is formed therein by lithography. Part ofthe silicon nitride film 103, and the SiN sidewall 110 are removed byetching using radical atoms or the like. Subsequently, the silicon oxidefilm 106 is etched by RIE or the like so as to align its level with thelevel of the crystalline silicon film 130. The etching rate is relatedto the thickness of a wiring layer to be formed later. Therefore, if theresistance of the wiring layer need not be so low, the etching rate maybe set lower than the above rate.

The resist film 136 is removed. Further, the steps shown in FIGS. 16Qand 16R are performed to obtain the semiconductor device shown in FIG.16T.

As described above, the 11th embodiment allows to simultaneously form aplurality of half-concave MOSFETs, electrically connect the sourceelectrode of a given MOSFET to the drain electrode of another one, andelectrically connect the source or drain electrode of a certain MOSFETto the gate electrode of another one.

According to the 11th embodiment, the silicon nitride film can be formedon only the gate electrode. The method and effects will be explained.

After the step shown in FIG. 16O, the W film 113 is etched back by RIEor SH processing, as shown in FIG. 16U. As shown in FIG. 16V, a siliconnitride film 137 is formed and flattened by CMP or resist etch-back.This flattening is performed until the polysilicon film 111 is exposed.

By performing the steps shown in FIGS. 16P to 16R, the semiconductordevice shown in FIG. 16W can be obtained. In the semiconductor devicewherein the silicon nitride film 137 is formed on only the gateelectrode, the electrode and the source/drain electrode are hardlyelectrically short-circuited. The reason will be explained withreference to FIG. 16X.

In FIG. 16X, an insulating film 138 such as a silicon oxide film isformed on the MOSFET shown in FIG. 16W. To form an opening in theinsulating film 138 in order to connect the source/drain electrode, aresist film (not shown) must be formed on the insulating film 138 bylithography. For example, when misalignment occurs, an opening may alsobe formed in the insulating film 138 above the gate electrode 113. Inthis case, if the opening of the insulating film 138 is filled with ametal 139 such as Al, the gate electrode 113 may be electricallyshort-circuited with the source/drain electrode 135. To the contrary, asshown in FIG. 16X, when the silicon nitride film 137 is formed on onlythe gate electrode 113, the gate electrode is covered with the siliconnitride film 137. Therefore, even if the opening is filled with themetal 139, the gate electrode 113 is not electrically short-circuitedwith the source/drain electrode 135. In addition, the gate insulatingfilm 132 made of a silicon oxide film is partially etched upon formingthe opening. However, since the upper surface of the gate electrode isat a position lower than the upper surface of the source/drainelectrode, the opening can be formed without excessively etching thegate insulating film 132.

The 12th embodiment of the present invention will be described below. Inthe ninth embodiment, the resistance of the source/drain/gate electrodeis decreased by adopting the elevated source/drain structure and using asilicide. If, however, a low resistance can be realized without using asilicide, no elevated source/drain structure need be employed. In the12th embodiment, the gate electrode is given with a polymetal structure,and the source/drain electrode is made of W, Al, or the like withoutemploying the elevated source/drain structure.

FIGS. 17A to 17H are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 12th embodiment of the present invention.

First, the same steps as described in the ninth embodiment withreference to FIGS. 13A to 13I are performed except that doping aconductive impurity in a polysilicon film 103 and activation areperformed after the step shown in FIG. 13A.

As shown in FIG. 17A, a W film 111 is formed. If necessary, a barrierlayer is formed before forming the W film 111. As shown in FIG. 17B, theW film 111 is flattened by CMP or the like. In this way, the entireregion except for a gate wiring formation region is covered with the Wfilm 111.

As shown in FIG. 17C, part of a sidewall 110, and an SiN film 108 areremoved by radical etching or RIE using the W film 111 as a mask. Atthis time, a thermal oxide film 107 functions as an etching stopper.

As shown in FIG. 17D, a silicon oxide film 106 is removed by RIE or thelike, and the polysilicon film 103 is etched back. In this case, thepolysilicon film 103 is not completely removed in order to realize agate electrode having a multilayered structure of polysilicon and ametal. As shown in FIG. 17E, the silicon oxide film 106 and the like areetched using the W film 111, the sidewall 110, and the polysilicon film103 as a mask. The silicon oxide film 106 is removed to such a degree asnot to expose the channel edge, i.e., the side surface of the siliconoxide film 102.

As shown in FIG. 17F, an Al film 113 is formed and flattened by CMP orthe like. If necessary, a barrier layer is formed before forming the Alfilm 113. This flattening is performed until the silicon oxide film 106is exposed. As a result, a MOSFET in which the gate electrode has amultilayered polymetal structure of polysilicon and Al, and thesource/drain electrode is made of W can be obtained.

According to the 12th embodiment, similar to the 10th embodiment, informing a plurality of MOSFETs, the source electrode of a given MOSFETand the drain electrode of another one, or the source or drain electrodeof a certain MOSFET and the gate electrode of another one can besimultaneously electrically connected. This will be explained withreference to FIGS. 17G and 17H.

By the above-mentioned method, the structure shown in FIG. 17D isobtained. As shown in FIG. 17G, a resist film 120 is formed, and anopening is formed therein by lithography. Thereafter, the W film 111 isetched using the silicon oxide film 106 as an etching stopper. Then, theSiN sidewall 110 is etched back to have a level almost equal to thelevel of the polysilicon film 103.

After the resist film 120 is removed, the steps described with referenceto FIGS. 17E and 17F are performed. With this processing, as shown inFIG. 17F, the source or drain electrode of a given MOSFET can beelectrically connected to the gate electrode of another one at the sametime as formation of a plurality of MOSFETs.

The 13th embodiment of the present invention will be described. In theninth and 12th embodiments, flattening by CMP is performed three times.In the 13th embodiment, the number of flattening steps can be reduced totwo by a resist recess technique. This will be explained with referenceto FIGS. 18A and 18B.

In the 12th embodiment, in the steps shown in FIGS. 17A and 17B, the Wfilm 111 is formed to cover the entire region except for a gate wiringregion. In the 12th embodiment, the SiN film 108 is etched using the Wfilm 111 as a mask. In contrast to this, according to the 13thembodiment, a resist film 111A is used instead of the W film 111, asshown in FIG. 18A.

More specifically, the same steps as described in the ninth embodimentwith reference to FIGS. 13A to 13I are performed except that doping aconductive impurity is doped in a polysilicon film 103 and activationare performed after the step shown in FIG. 13A.

As shown in FIG. 18A, a resist film 111A is formed. Then, the resist isrecessed to expose an SiN film 108, while the exposure amount isproperly controlled. Using the resist film 111A with the opening formedin this manner as a mask, the SiN film 108 can be selectively etched.

The steps described in the 12th embodiment with reference to FIGS. 17Dand 17E are performed. After that, the resist film 111A is removed, andthe step described in the 12th embodiment with reference to FIG. 17F isperformed to obtain a MOSFET in which the source/drain/gate electrode ismade of Al, as shown in FIG. 18B.

In the 13th embodiment, unlike the ninth, 11th , and 12th embodiments,the mask used in etching the SiN film 108 is made of a resist. For thisreason, in the 13th embodiment, no flattening need be executed to forman opening in the mask. According to this embodiment, the number of CMPsteps can be decreased, resulting in low manufacturing cost.

The process common to the ninth to 13th embodiments will be describedwith reference to FIGS. 19A and 19B. FIGS. 19A and 19B are sectionalviews, respectively, schematically showing the steps in manufacturing asemiconductor device according to the ninth and 13th embodiments of thepresent invention.

According to the ninth to 13th embodiments, a groove for burying asource/drain electrode, and a groove for burying a gate electrode areformed in different steps. That is, as shown in FIG. 19A, two types ofgrooves having different depths are formed in one major surface of asubstrate. In FIG. 19A, reference symbol R₁ denotes a source/drainelectrode formation region; R₂, a gate wiring formation region; and R₃,a device isolation region.

Each groove is filled with a mask material M₁. The mask material M₁ isselected to selectively remove the region R₂ with respect to thematerial M₁. The structure surface is flattened to expose the region R₂.

Then, the region R₂ is grooved using a thin film made of the material M₁as a mask. The groove formed in this way is filled with a material (notshown) used for forming a gate wiring layer. The structure surface isflattened to expose the device isolation region R₃.

When the mask material M₁ is an electrode material used for thesource/drain electrode, a MOSFET can be obtained by the above steps.When the mask material M₁ is a material to be removed, the mask materialM₁ is removed, the formed groove is filled with an electrode material,and the structure surface is flattened to obtain a MOSFET.

According to a method of manufacturing a semiconductor device of theninth to 13th embodiments, the gate wiring layer and the source anddrain electrodes can be self-aligned. In the ninth and 12th embodiments,the material M₁ is polysilicon and W, and used to form a source/drainelectrode. In the 11th and 13th embodiments, the material M₁ ispolysilicon and a resist, and removed before forming a source/drainelectrode. Note that in the 13th embodiment, after a gate insulatingfilm is formed, a gate wiring layer, and source and drain electrodes aresimultaneously buried.

According to the ninth to 13th embodiments, prior to formation of thesource/drain electrode, the gate structure and the device isolationinsulating film are so formed as to align their upper surface levelswith each other, and to form a groove crossing the gate structure anddivided by it. The source/drain electrode is formed in the groove,similar to the first to eighth embodiments. By the ninth to 13thembodiments, therefore, the same effects as those described in the firstto eighth embodiments can be obtained in addition to the own effects.Note that in the ninth to 13th embodiments, the same reference numeralsdenote the same parts unless otherwise specified.

In the first to 13th embodiments described above, the device isolationregion is formed to have an upper surface higher than the bottom surfaceof the source/drain electrode formation region. The effects obtainedfrom this structure will be explained in more detail with reference toFIGS. 20A, 20B, 21A, and 21B.

FIG. 20A is a sectional view schematically showing a method ofmanufacturing a conventional MOSFET. FIG. 20B is a sectional viewschematically showing a method of manufacturing a MOSFET according tothe first to 13th embodiments of the present invention. FIGS. 20A and20B show the intermediate steps for manufacturing a MOSFET having anelevated source/drain structure.

FIGS. 21A and 21B are graphs, respectively, showing the relationshipbetween the width of the device isolation region and the short yield inthe MOSFETs shown in FIGS. 20A and 20B. In FIGS. 21A and 21B, theabscissa represents a width d₁ or d₂ of the device isolation region 106,and the ordinate represents the short yield.

As shown in FIG. 20A, in the conventional MOSFET, the device isolationregion 106 is formed to be completely buried in the surface region ofthe substrate 101. When the crystalline silicon film 130 is formed onthe substrate 101 by selective epitaxial growth, the crystalline siliconfilm 130 also grows laterally. For example, when the crystalline siliconfilm 130 has a thickness t₁ of 50 nm, it also grows laterally by about50 nm. For this reason, as shown in FIG. 21A, the yield startsdecreasing at a width d₁ smaller than 0.2 μm in the device isolationregion 106, and to 0% at a width d₁ of 0.1 μm or less. That is,substantially all adjacent MOSFETs are short-circuited. Further, in theconventional method, the width d₁ must be at least 0.3 μm for athickness t₁ of 100 nm.

To the contrary, as shown in FIG. 20B, when the device isolation region106 is formed to have an upper surface higher than the substratesurface, no short-circuiting occurs between adjacent MOSFETs. In otherwords, even if the width d₂ of the device isolation region 106 decreasesto 0.1 μm, a high yield can be obtained independently of the thicknesst₂ of the crystalline silicon film 130, as shown in FIG. 21B.

In the future, the wiring layer in semiconductor devices will be formedat a width of about 0.1 μm. In this case, the width d₁ or d₂ mustdecrease to about 0.15 μm. In addition, a source/drain electrode and agate wiring layer made of cobalt silicide must be formed at a thicknessof 50 nm or more in order to realize a low resistance.

In forming a 50-nm thick silicide film, a crystalline silicon filmhaving a thickness of about 50 nm is consumed. Therefore, to realize ashallow junction at a depth of about 30 nm , and suppress the junctionleakage by silicide at the source and drain portions, the thickness t₁or t₂ must be 50 nm or more.

At a width d₁ of 0.15 μm, however, if a 50-nm thick crystalline siliconfilm 130 is formed by the conventional method, a high yield cannot beobtained. To obtain a high yield, the width d₁ must be 0.2 μm or more.This means that the integration degree cannot be increased from the onerealized in a semiconductor device having a wiring width of about 0.15μm. Moreover, micropatterning requires a lower resistance, so that thesilicide film must be made thick. In this case, by the conventionalmethod, the width d₁ must be increased. According to the conventionalmethod, the integration degree decreases along with micropatterning.

In contrast to this, according to the first to 13th embodiments of thepresent invention, the yield is independent of the width d₂ of thedevice isolation region 106 and the thickness t₂ of the crystallinesilicon film 130. Therefore, the integration degree can be increasedwithout decreasing the yield.

Furthermore, in the conventional method, source and drain electrodes tobe self-aligned must be made of silicide. In the first to 13thembodiments of the present invention, however, source and drainelectrodes can be made of a metal such as Al or Cu whose resistance islower than that of silicide. With the use of silicide, the crystallinesilicon film 130 must be made thick in order to prevent the junctionleakage. With the use of the low-resistance metal, the crystallinesilicon film 130 need not be made so thick, compared to the silicidefilm.

The 14th embodiment of the present invention will be described below. Amethod of manufacturing an nMOS will be explained, but a pMOS can alsobe manufactured by the same method by reversing the conductivity type ofan impurity.

FIGS. 22A to 22K are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 14th embodiment of the present invention.

As shown in FIG. 22A, a trench device isolation 206 is formed in thesurface region of one major surface of a substrate 201. Note that thesubstrate 201 is a p-type silicon substrate or a silicon substratewherein a p-type well region is formed. The device isolation 206 neednot always be a trench and may be formed by LOCOS. An oxide film 202having a thickness of about 8 nm is formed on the substrate 201. Then, athin film 203 made of, e.g., Si₃N₄ is formed on the oxide film 202.

As shown in FIG. 22B, the thin film 203 is patterned to form a dummygate wiring layer. The exposed portion of the oxide film 202 is removedwith a solution containing dilute hydrofluoric acid and the like.

As shown in FIG. 22C, silicon is selectively epitaxially grown using theexposed portion of the substrate 201 as a seed, thereby forming acrystalline silicon film 204′ having a thickness of about 20 nm. Aninsulating film 205 having a thickness of about 10 nm and made of SiO₂or the like is formed on the crystalline silicon film 204′ and the dummygate wiring layer 203 as shown in FIG. 22D. As+ ions are implanted inthe crystalline silicon film 204′ at an acceleration energy of 20 keVand a concentration of 1×10¹⁴ cm³ to form an impurity diffusion region.

As shown in FIG. 22E, a gate sidewall 207 made of an insulator such asSi₃N₄ is formed on the side surface of the dummy gate wiring layer 203via the insulating film 205. Using the gate sidewall 207 as a mask, As⁺ions and the like are implanted in the crystalline silicon film 204′,thereby forming an extension 204 below the gate sidewall 207. Further,an n⁺-type diffusion region 208 is formed adjacent to the extension 204.Note that the extension 204 is made shallower than the n⁺-type diffusionregion 208. The extension 204 and the n⁺-type diffusion region 208constitute source and drain diffusion layers.

In this step, the insulating film 205 is used as an etching stopper foretching performed in formation of the gate sidewall 207, and inaddition, functions to prevent channeling upon ion implantation forforming the n⁺-type diffusion region 208. The effective depth of then⁺-type diffusion region 208 formed in the above fashion, i.e., thedepth from the oxide film 202 is smaller than an actual depth by thethickness of the extension 204. When a silicide film is to be formed inthe source/drain region by SALICIDE method, the exposed portion of theinsulating film 205 is removed, and a metal film (not shown) made of Ti,Co, or the like is formed after the above steps. The metal is reactedwith Si constituting the n⁺-type diffusion region 208 by RTA or thelike, and the unreacted metal is removed by, e.g., a solution mixturecontaining sulfuric acid and hydrogen peroxide. As a result, a silicidefilm can be formed.

As shown in FIG. 22F, an insulating film 209 made of SiO₂ or the like isformed on the entire surface of the substrate 201 in which the n⁺-typediffusion region 208 is formed. As shown in FIG. 22G, the resultantsurface is flattened by CMP or the like. This flattening is performednot to expose the gate sidewall 207 and performed to expose the topsurface of the dummy gate wiring layer 203.

As shown in FIG. 22H, the dummy gate wiring layer 203 is removed. Whenthe dummy gate wiring layer 203 is made of Si₃N₄, and the insulatingfilm 209 is made of SiO₂, as in the 14th embodiment, the dummy gatewiring layer 203 can be selectively removed with hot phosphoric acid. Inthe 14th embodiment, the dummy gate wiring layer 203 is made of Si₃N₄,and the insulating films 205 and 209 are made of SiO₂. However, othermaterials are also available as far as only the dummy gate wiring layer203 can be selectively removed in the step shown in FIG. 22G. Note thatonly the dummy gate wiring layer 203 is desirably removed by selectiveetching without damaging the channel portion. Further, ions may beimplanted to adjust the threshold of the transistor. In this case,increase of the junction capacitance of the source/drain region isprevented because of that ions can be selectively implanted in only thechannel portion.

As shown in FIG. 22I, the exposed portion of the insulating film 205,and the oxide film 202 are removed with adilute-hydrofluoric-acid-containing solution or the like. As shown inFIG. 22J, a gate insulating film 210, a reaction preventing film 211,and a gate electrode material film 212 are sequentially stacked.

The gate insulating film 210 is preferably made of a high-dielectriccompound such as Ta₂O₅ and BST. The gate insulating film 210 isdesirably formed by CVD. Using CVD, the gate insulating film 210 can beformed in conformity with the groove shape.

The reaction preventing film 211 is formed to prevent reaction betweenthe gate insulating film 210 and the gate electrode material film 212.Therefore, when the gate insulating film 210 hardly thermally reactswith the gate electrode material film 212, or the gate electrodematerial hardly diffuses to the gate insulating film 210, the reactionpreventing film 211 need not always be formed. The material constitutingthe reaction preventing film 211 is determined in accordance with acombination of the materials constituting the gate insulating film 210and the gate electrode material. In general, the reaction preventingfilm is made of a metal nitride such as TiN, TaN, or WN_(X), or aternary compound containing a metal, nitrogen, and silicon.

The gate electrode material film 212 is preferably made of a materialmainly containing a metal such as W or Al. The gate electrode materialfilm 212 is desirably formed by CVD. Using CVD, the gate electrodematerial film 212 can be formed into a preferable shape. Alternatively,PVD may be employed so long as the gate electrode material film 212 canbe formed into a preferable shape.

By the following method, the gate electrode material film 212 can bemade of Al. More specifically, the groove is filled with amorphoussilicon by low-pressure CVD, and Al and Ti are deposited on theamorphous silicon. The resultant structure is heated to a temperature ofabout 450° C. to diffuse Si in the groove into the Al layer. Thediffused Si reacts with Ti to produce TiSi_(x). TiSi_(x) is a stablecompound and immobile. Consequently, Si in the groove is substitutedwith Al.

After the step shown in FIG. 22J, the structure surface is flattened byCMP or the like, as shown in FIG. 22K. This flattening is performeduntil the insulating film 209 is exposed. In this way, the gateelectrode 212 is formed in the groove.

According to the 14th embodiment, since a overwrap between thesource/drain diffusion layers and the gate electrode can be reduced, theparasitic capacitance can be reduced between the gate electrode and thesource/drain diffusion layers. Moreover, according to the 14thembodiment, the source/drain diffusion layers can be made sufficientlythick, and its effective depth can be decreased. Even upon a reductionin size, punch-through can be prevented.

The 15th embodiment of the present invention will be described. The 15thembodiment is different from the 14th embodiment in that a CMOS ismanufactured, and by a method of doping a conductive impurity forforming an extension.

FIGS. 23A to 23D are sectional views, respectively, schematicallyshowing the steps in manufacturing a semiconductor device according tothe 15th embodiment of the present invention.

As shown in FIG. 23A, a device isolation 206, a p-type well region 221,and an n-type well region 222 are formed in the surface region of asilicon substrate 201. An oxide film 202, and a thin film 203 made of,e.g., Si₃N₄ are sequentially formed on the surface of the substrate 201in which the device isolation 206 and the like are formed.

As shown in FIG. 23B, the thin film 203 above the p-type well region 221is patterned to form a dummy gate wiring layer 203A. As shown in FIG.23C, the exposed portion of the oxide film 202 is removed with adilute-hydrofluoric-acid-containing solution or the like. Using theexposed surface of the substrate 201 as a seed, silicon is selectivelyepitaxially grown to form a crystalline silicon film 204A having athickness of about 20 nm. Note that this selective epitaxial 5 growth isperformed in an atmosphere containing AsH₃ gas and PH₃ gas, therebydoping an n-type impurity in the crystalline silicon film 204A.Thereafter, a silicon oxide film 205 having a thickness of about 10 nmis formed by oxidizing the surface of the crystalline silicon film 204Aor performing CVD or the like.

As shown in FIG. 23D, the thin film 203 above the n-type well region 222is patterned to form a dummy gate wiring layer 203B. By the abovemethod, the exposed portion of the oxide film 202 is removed with adilute-hydrofluoric-acid-containing solution or the like. Using theexposed surface of the substrate 201 as a seed, silicon is selectivelyepitaxially grown to form a crystalline silicon film 204B having athickness of about 20 nm. Note that this selective epitaxial growth isperformed in an atmosphere containing B₂H₆ gas, thereby doping a p-typeimpurity in the crystalline silicon film 204B. Then, a silicon oxidefilm (not shown) having a thickness of about 10 nm is formed byoxidizing the surface of the crystalline silicon film 204B or performingCVD or the like.

The steps described in the 14th embodiment with reference to FIGS. 22Eto 22K are performed to obtain a MISFET.

As described above, according to the 15th embodiment, the effectsdescribed in the 14th embodiment can be obtained. When ions areimplanted to form an extension, the total of three PEPs (Photo EngravingProcesses) are necessary in patterning and doping the gate electrode.According to the 15th embodiment, however, the number of PEPs can bereduced to two. In ion implantation, the impurity concentrationdecreases from the substrate surface to a deeper portion. In the 15thembodiment, however, no concentration gradient of the conductiveimpurity is generated. Therefore, an extension uniformly containing theconductive impurity at a high concentration can be formed. According tothe 15th embodiment, the parasitic resistance can be further reduced.

Additional advantages and modifications will readily occur to thoseskilled in the art. Therefore, the invention in its broader aspects isnot limited to the specific details and representative embodiments shownand described herein. Accordingly, various modifications may be madewithout departing from the spirit or scope of the general inventiveconcept as defined by the appended claims and their equivalents.

What is claimed is:
 1. A method of manufacturing a semiconductor device,comprising: a) forming, on one major surface of a substrate, a gatestructure selected from the group consisting of a first gate structurecomprising a dummy gate wiring layer and a dummy gate electrode, and asecond gate structure comprising a gate wiring layer and a gateelectrode, each of the gate wiring layer and the gate electrode beingprovided with an insulating film at least on a bottom surface thereof,and a device isolation insulating film having a first groove, such thatsaid dummy gate electrode or said gate electrode divides said firstgroove, and such that an upper surface level of said gate structure isnot higher than an upper level of said device isolation insulating film;and b) forming source and drain electrodes in the first groove by use offilm forming and flattening, wherein said dummy gate wiring layer orsaid gate wiring layer is formed on the device isolation insulatingfilm, connected to said dummy gate electrode or said gate electrode, andcrossing said first groove.
 2. A method according to claim 1, furthercomprising respectively forming a source diffusion layer and draindiffusion layer in a surface region of said substrate corresponding tothe first groove before the formation of said source and drainelectrodes.
 3. A method according to claim 1, wherein the formation ofsaid source and drain electrodes comprises: forming, on one entire majorsurface of said substrate, a first thin film made of either one of amaterial constituting said source and drain electrodes and a materialused to form said source and drain electrodes; and removing a portion ofsaid first thin film located outside the first groove by using CMP.
 4. Amethod according to claim 1, wherein said gate structure is the firstgate structure, and the method further comprises: removing said firstgate structure to form a second groove after the formation of saidsource and drain electrodes; and forming an insulating film, a gateelectrode, and a gate wiring layer in the second groove so that saidgate electrode divides the gate wiring layer and positions between saidsource electrode and said drain electrode, and so that said insulatingfilm is interposed between said gate wiring layer and an inner wall ofthe second groove.
 5. A method according to claim 4, wherein said gateelectrode and said gate wiring layer are simultaneously formed in onepiece by: forming a second thin film made of either one of a materialconstituting said gate wiring layer and material used to form said gatewiring layer, on one entire major surface of said substrate; andremoving a portion of said second thin film located outside the secondgroove by using CMP.
 6. A method according to claim 4, furthercomprising, before the formation of said insulating film and said gatewiring layer: doping, with a conductive impurity, a surface region ofsaid substrate corresponding to the second groove; and forming asemiconductor film on a bottom surface of the second groove by usingepitaxial growth.
 7. A method according to claim 1, wherein theformation of said gate structure and said device isolation insulatingfilm comprises: forming said device isolation insulating film on onemajor surface of said substrate; forming a third groove in said deviceisolation insulating film; forming, on one entire major surface of saidsubstrate, a third thin film made of a material constituting said gatestructure; removing a portion of said third thin film located outsidethe third groove by using CMP; and forming the first groove, at least apart of the sidewall of which is constituted by said device isolationinsulating film, so as to cross the gate structure.
 8. A methodaccording to claim 1, wherein said source and drain electrodes are madeof a metal.
 9. A method according to claim 1, wherein said gatestructure is the second gate structure, and said gate electrode and saidgate wiring layer are made of a metal.
 10. A method of manufacturing asemiconductor device, comprising: a) forming, on one major surface of asubstrate, a gate structure comprising either one of a dummy gateelectrode and a gate electrode which is provided with an insulating filmat least on a bottom surface thereof, and a device isolation insulatingfilm having a first groove, such that said dummy gate electrode or saidgate electrode divides said first groove, and such that an upper surfacelevel of said gate structure is not higher than an upper level of saiddevice isolation insulating film; and b) forming source and drainelectrodes in the first groove by use of film forming and flattening,wherein the formation of said gate structure and said device isolationinsulating film comprises forming a dummy wiring layer which ispositioned above part of said device isolation insulating film, and saidgate structure, and has an upper surface level higher than the uppersurface level of said device isolation insulating film.
 11. A methodaccording to claim 10, further comprising, before the formation of saidsource and drain electrodes: forming a fourth thin film on one entiremajor surface of said substate; polishing said fourth thin film andexposing an upper surface of said dummy wiring layer; and removing saiddummy wiring layer to form a fourth groove in said fourth thin film. 12.A method according to claim 11, further comprises removing at least apart of an exposed portion of said device isolation insulating film inthe fourth groove to form an eighth groove in a bottom of said fourthgroove, between the formation of the fourth groove and the formation ofsaid source and drain electrodes.
 13. A method according to claim 11,wherein said gate structure is the dummy gate electrode, and the methodfurther comprises, between the formation of said fourth groove and theformation of said source and drain electrodes, removing said dummy gateelectrode to form a seventh groove in a bottom of said fourth groove;and forming a gate electrode in the fourth groove.
 14. A methodaccording to claim 13, further comprising, after the formation of saiddevice isolation insulating film and said gate structure: removing aportion of said device isolation insulating film to form a fifth groove;and forming, in the fifth groove, a connection wiring layer connected toat least one of said source electrode, said drain electrode, and saidgate wiring layer, wherein the formation of said gate wiring layer andthe formation of said connection wiring layer are performedsimultaneously.
 15. A method according to claim 11, wherein said fourththin film is made of either one of a material constituting said sourceand drain electrodes and material used to form said source and drainelectrodes.
 16. A method according to claim 11, further comprisingremoving said fourth thin film before the formation of said source anddrain electrodes.
 17. A method according to claim 11, furthercomprising, after the formation of said device isolation insulating filmand said gate structure: removing a portion of said device isolationinsulating film to form a fifth groove; and forming, in the fifthgroove, a connection wiring layer connected to at least one of saidsource electrode, said drain electrode, and said gate wiring layer. 18.A method according to claim 17, wherein the formation of said connectionwiring layer and the formation of said source and drain electrodes areperformed simultaneously.
 19. A method according to claim 10, furthercomprising respectively forming a source diffusion layer and a draindiffusion layer in a surface region of said substrate corresponding tothe first groove before the formation of said source and drainelectrodes.
 20. A method according to claim 10, wherein the formation ofsaid source and drain electrodes comprises: forming, on one entire majorsurface of said substrate, a first thin film made of either one of amaterial constituting said source and drain electrodes and a materialused to form said source and drain electrodes; and removing a portion ofsaid first thin film located outside the first groove by using CMP. 21.A method according to claim 10, wherein said source and drain electrodesare made of a metal.
 22. A method according to claim 10, wherein saidgate structure comprises said gate electrode, and said gate electrodeand said gate wiring layer are made of a metal.
 23. A method ofmanufacturing a semiconductor device, comprising: a) forming, on onemajor surface of a substrate, a gate structure comprising either one ofa dummy gate electrode and a gate electrode which is provided with aninsulating film at least on a bottom surface thereof, and a deviceisolation insulating film having a first groove, such that said dummygate electrode or said gate electrode divides said first groove, andsuch that an upper surface level of said gate structure is not higherthan an upper level of said device isolation insulating film; b) forminga semiconductor film using epitaxial growth on a bottom surface of thefirst groove; c) respectively forming source and drain diffusion layersin said semiconductor film groove; d) forming source and drainelectrodes in the first groove by use of film forming and flatteningafter the formation of the source and drain diffusion layers.
 24. Amethod according to claim 23, further comprising respectively forming asource diffusion layer and drain diffusion layer in a surface region ofsaid substrate corresponding to the first groove before the formation ofsaid source and drain electrodes.
 25. A method according to claim 23,wherein the formation of said source and drain electrodes comprises:forming, on one entire major surface of said substrate, a first thinfilm made of either one of a material constituting said source and drainelectrodes and a material used to form said source and drain electrodes;and removing a portion of said first thin film located outside the firstgroove by using CMP.
 26. A method according to claim 23, wherein saidsource and drain electrodes are made of a metal.
 27. A method accordingto claim 23, wherein said gate structure comprises said gate electrode,and said gate electrode and said gate wiring layer are made of a metal.28. A method of manufacturing a semiconductor device, comprising: a)forming, on one major surface of a substrate, a gate structurecomprising either one of a dummy gate electrode and a gate electrodewhich is provided with an insulating film at least on a bottom surfacethereof, and a device isolation insulating film having a first groove,such that said dummy gate electrode or said gate electrode divides saidfirst groove, and such that an upper surface level of said gatestructure is not higher than an upper level of said device isolationinsulating film; and b) forming source and drain electrodes in the firstgroove by use of film forming and flattening, wherein the formation ofsaid gate structure and said device isolation insulating film comprises:forming, on one entire major surface of said substrate, a third thinfilm made of a material constituting said dummy gate wiring layer;forming a second forward-tapered groove in said third thin film; formingsaid device isolation insulating film an one major surface of saidsubstrate; removing a portion of said device isolation insulating filmlocated outside the second groove by using CMP; and anisotropicallyetching said third thin film to simultaneously form said gate structureand first groove, and a sidewall on a side surface of said deviceisolation insulating film.
 29. A method according to claim 28, furthercomprising respectively forming a source diffusion layer and draindiffusion layer in a surface region of said substrate corresponding tothe first groove before the formation of said source and drainelectrodes.
 30. A method according to claim 28, wherein the formation ofsaid source and drain electrodes comprises: forming, on one entire majorsurface of said substrate, a first thin film made of either one of amaterial constituting said source and drain electrodes and a materialused to form said source and drain electrodes; and removing a portion ofsaid first thin film located outside the first groove by using chemicalmechanical polishing.
 31. A method according to claim 28, wherein saidsource and drain electrodes are made of a metal.
 32. A method accordingto claim 28, wherein said gate structure comprises said gate electrode,and said gate electrode and said gate wiring layer are made of a metal.